Kingcera NMC-ZTA material
By Hunan Kingcera Engineering Co., Ltd.
NMC-ZTA. Wear lining for high-impact bulk-material conveying equipment under normal-temperature conditions. Ceramic-phase density: ≥4.15 g/cm³; Ceramic-phase Rockwell hardness: ≥90 HRA.
Specifications
| Attribute | Value | Conditions | Source |
|---|---|---|---|
| Ceramic-phase density | ≥4.15 g/cm³ | Source ZTA ceramic table; not the composite ceramic/rubber/steel liner bulk density | Kingcera NMC-ZTA original component-specific technical and application tables |
| Ceramic-phase Rockwell hardness | ≥90 HRA | Source ZTA ceramic table | Kingcera NMC-ZTA original component-specific technical and application tables |
| Ceramic-phase flexural strength | 450 MPa | Source ZTA ceramic table; test method not supplied | Kingcera NMC-ZTA original component-specific technical and application tables |
| Ceramic-phase compressive strength | 2500 MPa | Source ZTA ceramic table; test method not supplied | Kingcera NMC-ZTA original component-specific technical and application tables |
Sources and updates
Scope of this page: One documented material/product family. Technical values retain the stated material-component scope; not a whole equipment/assembly guarantee. Stock shapes, dimensions, backing thickness, mounting options and generic material aliases are not additional products. Test temperature and method are unspecified unless explicitly stated; no validated service life, wear-rate comparison, chemical compatibility, safety approval or independent verification asserted. Source750°C ceramic-only figure is not applied to its room-temperature rubber-backed liner; conflicting/incorrect fracture-toughness units omitted.
Kingcera NMC-ZTA original component-specific technical and application tables
Original publication · Kingcera
Source accessed: 27 October 2026
Content updated 27 October 2026. Source dates describe the documents or the recorded access to them.
How information is documented